<p><span quot;font-size: small; font-family: 幼圆;">详细信息：</span></p> <p><span quot;font-family: 幼圆;"><span quot;font-size: small;">牌号：6061铝合金</span><br /></span></p> <p><span quot;font-size: small; font-family: 幼圆;">典型用途<br />　　代表用途包括航天固定装置、电器固定装置、通讯领域，也广泛应用于自动化机械零件、准确加工、模具制造、电子及准确仪器、SMT、PC板焊锡载具等等。</span></p> <p><span quot;font-size: small; font-family: 幼圆;">化学成分<br />　　化学成分(%): </span></p> <p><span quot;font-size: small; font-family: 幼圆;">　　Cu :0.15～0.4 </span></p> <p><span quot;font-size: small; font-family: 幼圆;">　　Mn :0.15 </span></p> <p><span quot;font-size: small; font-family: 幼圆;">　　Mg :0.8～1.2</span></p> <p><span quot;font-size: small; font-family: 幼圆;"> 　  Zn :0.25</span></p> <p><span quot;font-size: small; font-family: 幼圆;"> 　   Cr :0.04～0.35</span></p> <p><span quot;font-size: small; font-family: 幼圆;"> 　　Ti :0.15</span></p> <p><span quot;font-size: small; font-family: 幼圆;"> 　　Si :0.4～0.8</span></p> <p><span quot;font-size: small; font-family: 幼圆;"> 　　Fe :0.7 </span></p> <p><span quot;font-size: small; font-family: 幼圆;">　　 Al :余量 　　</span></p> <p><span quot;font-size: small; font-family: 幼圆;">力学性能<br />　　6061铝合金性能: 6061的较限抗拉强度为124 MPa 　　</span></p> <p><span quot;font-size: small; font-family: 幼圆;">                            受拉屈服强度 55.2 MPa 　　</span></p> <p><span quot;font-size: small; font-family: 幼圆;">                             延伸率25.0 % 　　 </span></p> <p><span quot;font-size: small; font-family: 幼圆;">                           弹性系数68.9 GPa 　　</span></p> <p><span quot;font-size: small; font-family: 幼圆;">                          弯曲较限强度228 MPa 　　</span></p> <p><span quot;font-size: small; font-family: 幼圆;">                         Bearing Yield Strength 103 MPa 　　</span></p> <p><span quot;font-size: small; font-family: 幼圆;">                          泊松比0.330 </span></p> <p><span quot;font-size: small; font-family: 幼圆;">                     　　疲劳强度 62.1 MPa</span></p> <p><span quot;font-size: small; font-family: 幼圆;">热处理工艺：<br />　　1）快速退火：加热温度350～410℃;随材料有效厚度的不同，保温时间在30～120min之间;空气或水冷。</span></p> <p><span quot;font-size: small; font-family: 幼圆;">     2）高温退火：加热温度350～500℃;成品厚度≥6mm时，保温时间为10～30min、＜6mm时，热透为止;空气冷。</span></p> <p><span quot;font-size: small; font-family: 幼圆;">     3）低温退火：加热温度150～250℃;保温时间为2～3h;空气或水冷。<br /></span></p>